Glass Fiber Reinforced PA66 Pellets Polyamide for Thermal Break Strip
Product Introduction:
Polyamide 6.6 granules reinforced by fiberglass, with special additives, are blended and extruded by a twin-screw extrusion machine. It is more suitable for the extrusion of heat insulation strips. Compared with ordinary granules, it is more conducive to forming. It has certain advantages in speed, surface finish, and yield. The performance of the nylon insulating strip produced from this material meets national standards. It can not only be customized according to customer requirements, far exceeding the national standard, but it can also add high-efficiency flame retardant to achieve the purpose of flame retardant.
Advantage:
Our company has devoted more than ten years to the research and development and production of nylon extruding profiles. According to customer reaction, using our PA66 granules for production can get high yield, easy start-up, and get less scrap in the early start-up stage. There will be no lack or incomplete of profiles in the production process, thus avoiding material waste, saving customer costs and improving production efficiency.
PA66 Features
1. It has excellent mechanical properties, high strength, high toughness.
2. The material has excellent coloring ability, can achieve various requirements of color matching
3. The shrinkage rate of PA66 is between 1% and 2%. The addition of glass fiber additives can reduce the shrinkage rate to 0.2%~1%. The shrinkage ratio is large in the flow direction and in the direction perpendicular to the flow direction.
4. PA66 is resistant to many solvents, but is less resistant to acids and other chlorinating agents.
5. PA66 excellent flame retardant performance, by adding different flame retardants can achieve different levels of flame retardant effect.
Polywell PA66 Granules Performance Table
| NO. |
Item |
Unit |
GB/T 23615.1-2009 |
PW-Technical specification |
| |
Material Properties |
| 1 |
Density |
g/cm3 |
1.3±0.05 |
1.28-1.35 |
| 2 |
Linear expansion coefficient |
K-1 |
(2.3-3.5)×10-5 |
(2.3-3.5)×10-5 |
| 3 |
Vicat softening temperature |
ºC |
≥230ºC |
≥233ºC |
| 4 |
Melting point |
ºC |
≥240 |
≥240 |
| 5 |
Testing for tensile cracks |
- |
No cracks |
No cracks |
| 6 |
Shore hardness |
- |
80±5 |
80-85 |
| 7 |
Impact strength(Unnotched) |
KJ/m2 |
≥35 |
≥38 |
| 8 |
Tensile strength(longitudinal) |
MPa |
≥80a |
≥82a |
| 9 |
Elasticity modulus |
MPa |
≥4500 |
≥4550 |
| 10 |
Elongation at break |
% |
≥2.5 |
≥2.6 |
| 11 |
Tensile strength(transverse) |
MPa |
≥70a |
≥70a |
| 12 |
High temperature tensile strength(transverse) |
MPa |
≥45a |
≥47a |
| 13 |
Low temperature tensile strength(transverse) |
MPa |
≥80a |
≥81a |
| 14 |
Water resistance tensile strength(transverse) |
MPa |
≥35a |
≥35a |
| 15 |
Aging resistance tensile strength(transverse) |
MPa |
≥50a |
≥50a |
1.Sample water content less than 0.2% by weight.
2.Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.
3.The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
About color:
The color of our products is black, but we also can customize according to customers' requirements.
Application:
Widely used in machinery, instrumentation, automotive parts, electrical and electronics, railways, household appliances, telecommunications, textile, sports and leisure goods, pipes and precision engineering products.
Packaging & Delivery:
Packaging details: 25kg/bag
Delivery details: Shipped in 7-15 working days after payment.
Our Company:
Related Products we can provide:
| Thermal Break Strip Extruding Machine |
Thermal Break Strip |
Extrusion Mold |
Please feel free to contact us if you have any questions.