Plastic Raw Material Glass Fiber Nylon 66 Particles Polyamide 66 Pellets For Hear Insulation Bar
Product Introduction:
Polyamides are among the most important and proven technical thermoplastics, known for their heat resistance, stiffness and high mechanical stability.
Polyamides can be classified into different types, with PA 6, PA 6.6 and PA 12 most established on the market. Alongside ABS and PP compounds they are among the most widely used plastics, found across several sectors including the automotive, mechanical engineering, structural and installation engineering, photovoltaics and electrical engineering industries.
Glass fiber is a material consisting of numerous extremely fine fibers of glass.
Glass fibres are used as reinforcement of polymers in various fields such as aerospace, automobile, marine, sporting and leisure goods, and construction and civil engineering. One of the principal advantages of using glass fibres for reinforcement of polymers is their high performance per cost ratio.
Our company use PA 6.6 and glass fiber to produce PA66GF25 granules, which is the most suitable raw material for polyamide thermal break strips production.
Advantage:
Our company has devoted more than ten years to the research and development and production of nylon extruding profiles. According to customer reaction, using our PA66 granules for production can get high yield, easy start-up, and get less scrap in the early start-up stage. There will be no lack or incomplete of profiles in the production process, thus avoiding material waste, saving customer costs and improving production efficiency.
About color:
The color of our products is black, but we also can customize according to customers' requirements.
What is GF in plastic material?
Glass-filled nylon is a synthetic polyamide thermoplastic and it's one of the most important materials used in engineering thanks to its strength and heat resistance. It's made by adding powdered glass to nylon resin or by extruding the plastic with glass fibers.
Polywell PA66 Granules Performance Table
| NO. |
Item |
Unit |
GB/T 23615.1-2009 |
PW-Technical specification |
| |
Material Properties |
| 1 |
Density |
g/cm3 |
1.3±0.05 |
1.28-1.35 |
| 2 |
Linear expansion coefficient |
K-1 |
(2.3-3.5)×10-5 |
(2.3-3.5)×10-5 |
| 3 |
Vicat softening temperature |
ºC |
≥230ºC |
≥233ºC |
| 4 |
Melting point |
ºC |
≥240 |
≥240 |
| 5 |
Testing for tensile cracks |
- |
No cracks |
No cracks |
| 6 |
Shore hardness |
- |
80±5 |
80-85 |
| 7 |
Impact strength(Unnotched) |
KJ/m2 |
≥35 |
≥38 |
| 8 |
Tensile strength(longitudinal) |
MPa |
≥80a |
≥82a |
| 9 |
Elasticity modulus |
MPa |
≥4500 |
≥4550 |
| 10 |
Elongation at break |
% |
≥2.5 |
≥2.6 |
| 11 |
Tensile strength(transverse) |
MPa |
≥70a |
≥70a |
| 12 |
High temperature tensile strength(transverse) |
MPa |
≥45a |
≥47a |
| 13 |
Low temperature tensile strength(transverse) |
MPa |
≥80a |
≥81a |
| 14 |
Water resistance tensile strength(transverse) |
MPa |
≥35a |
≥35a |
| 15 |
Aging resistance tensile strength(transverse) |
MPa |
≥50a |
≥50a |
1.Sample water content less than 0.2% by weight.
2.Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.
3.The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
Application:
Widely used in machinery, instrumentation, automotive parts, electrical and electronics, railways, household appliances, telecommunications, textile, sports and leisure goods, pipes and precision engineering products.
Packaging & Delivery:
Packaging details: 25kg/bag
Delivery details: Shipped in 5-7 working days after deposit
Our Company:
Related Products we can provide:
| Thermal Break Strip Extruding Machine |
Thermal Break Strip |
Extrusion Mold |
Please feel free to contact us if you have any questions.